Pengaruh Temperatur Pemanasan dan Pendinginan Terhadap Sifat Mekanik Pada Proses Annealing Baja AISI410 Setelah Pengerasan

Main Article Content

BAYU PRANOTO Subagiyo Subagiyo Samsul Hadi

Abstract

Stainless steel has good mechanical properties compared to other materials for strength and hardness, usually will experience an increase in hardness after hardening. The purpose of this study was to obtain information about: Value of hardness and strength Impact of martensitic stainless steel annealed with variations in temperature and cooling. The research method used is an experimental method, namely by annealing martensitic stainless steel with variations in temperature and cooling rate. The results were tested for Impact and hardness using the Rockwell C (HRC) method with the category of Research Infrastructure development and science and technology in the field of Mechanical Engineering. The research results are expected to be used as an alternative to improve the mechanical properties of materials, especially in the annealing process. The level of technological readiness to be achieved: 2, because in this study a model is made to test the truth of the basic principle that the hardness level of martensitic steel in annealing is influenced by varying temperatures and cooling.

Downloads

Download data is not yet available.

Article Details

How to Cite
PRANOTO, B., Subagiyo, S., & Hadi, S. (2022). Pengaruh Temperatur Pemanasan dan Pendinginan Terhadap Sifat Mekanik Pada Proses Annealing Baja AISI410 Setelah Pengerasan. Jurnal Energi Dan Teknologi Manufaktur (JETM), 5(02), 23-28. https://doi.org/https://doi.org/10.33795/jetm.v5i02.132
Section
Articles

References

[1] Prasetyo, M. A., Anwar, M. S., Mahruri, E., Agustiningtyas, D. T., Noviana, R. C., Laksono, A. D. 2020. Pengaruh Perlakuan Panas Baja Tahan Karat Martensitik AISI 410 Terhadap Struktur Mikro dan Ketahanan Korosi Di Lingkungan Simulasi Geothermal dalam Larutan Artificial Brine. Jurnal Teknik. p-ISSN: 0852-1697. e-ISSN: 240-9919 41(2). 179-185
[2] Puspasari, V., Prasetyo, M. A., Hala, J. V. T., Anwar, M. S., Herbirowo, S., Mabruri, E. 2020. Pengaruh Annealing Terhadap Kekerasan dan Struktur Mikro Baja Tahan Karat AISI 410-3Mo-3Ni. Majalah Ilmu dan Teknologi. p-ISSN: 0126-3188. e-ISSN: 2443-3926. 2. 75-82
[3] Sinaga, A. J., Simanjuntak, S. L. M. H., Manurung, C. S. P. 2020. Analisa Laju Korosi dan Kekerasan Pada Stainless Steel 316L Dalam Larutan 10% NaCl dengan Variasi Waktu Perendaman. SJoME. e-ISSN: 2685-8916. I(2). 92-99
[4] Fikara, F. A., Siswanto, R. 2021. Pengaruh Holding Time dan Media Pendingin Pada Carburizing Material SUS 630 Terhadap Nilai Kekerasan dan Struktur Mikro. ROTARY. p-ISSN: 2721-6225. e-ISSN: 2745-6331. 3(1). 81-94
[5] Herizen, D., Siswanto, R. 2020. Pengaruh Variasi Holding Time dan Media Pendingin Terhadap Kekerasan dan Struktur Mikro Baja SUS 630 Metode Hardening. ROTARY. p-ISSN: 2721-6225. e-ISSN: 2745-6331. 2(2). 149-160
[6] Sarigih, D. J. P., Subagyo. 2021. Pengaruh Variasi Waktu Penahanan dan Tebal Benda Kerja Hasil Quenching Terhadap Sifat Mekanik Baja Stainless Steel Martensit. Jurnal Teknik: Ilmu dan Aplikasi. 02(1). 15-19
[7] Hadi, S. 2016. Teknologi Bahan. Andi Offset. Jogyakarta